FRAGOM G/458 NAT
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KHg8yu_FRAGOM-G-458-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM G/458 NAT: flame retardant crosslinkable compound having good temperature index and oxygen index, suitable for cable sheathing and insulation. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 SCU REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 We suggest to use the compound to produce cables with size not more than 10 mm2. Certify: BS 7655 EI5,VDE 0207 HM1,BS 4066,AZ/NZS X-HF-110,R-HF-110,HF-110-R |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 15 - 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 11.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | > 160 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | 19 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | -16 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 200°C | 90 | % | IEC 60811 |
| Residual : 200°C | 0.0 | % | IEC 60811 |
| Temperature index 2 | > 290 | °C | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | µS/mm | IEC 60754-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | % | IEC 60754-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+14 | ohms·cm | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 155 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 195 | °C | |
| Cylinder Zone 5 Temp. | 205 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin in hot water at 85/90°C f or two hours (up to 1 mm thickness) Steam treatment at 0,15 bar for 6/8 hours |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| 2 . | 21% O2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9740 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Dugdale PVC Flexible Extrusion - Shore A 74 Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| ESENTTIA 01R25 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| Jiangsu Sinarise JM9331 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| FUDOWPREMIX® FP100F typeA | Fudow Co., Ltd. | Polyester, TS | FUDOWPREMIX® |