SABIC® HDPE B4406
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KGO3Td_SABIC-HDPE-B4406.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®HDPE B4406 is a high-density polyethylene product,. It can be processed by blow molding and is available in Europe. SABIC®The application areas of HDPE B4406 include container and food contact applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.944 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 6.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.20 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 750 | MPa | ISO 527-2/1BA/1 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 21.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 33.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 1000 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 25 | kJ/m² | ISO 180/1A |
| 23°C | 28 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 64.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 124 | °C | ISO 306/A50 |
| Additional Information |
|---|
| Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >1000%Melt Flow Rate, ISO 1133, 190°C/2.16 kg: <0.1 g/10 minESCR, SABIC Method, Compression Molded, Determined in Rhodacal-DS10 at 75°C, 3 N/mm², thickness 1mm: 200hrMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 129°CEnthalpy Change, DIN 53765: 180J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bionolle™ 1903 MD | Showa Denko K.K. | Biodeg Polymers | Bionolle™ |
| ColorRx® PPE-0800RX | LTL Color Compounders, Inc. | PPE | ColorRx® |
| Geon™ Vinyl Flexible A80U0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| E-Pos 327H | Epocat Nederland BV | Epoxy | E-Pos |
| POLYfill PPH GK8020D | Polykemi AB | PP Homopolymer | POLYfill |