KPOL-PP K-PPH 8.5I

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KG5dd7_KPOL-PP-K-PPH-8-5I.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Homopolymer

Applications

The KPOL® is a medium flow homopolymer used for general purpose injection moulding applications.

It is suitable for production of complex articles with long flow paths and thin walls. Typical applications are Sealed or flip-top closures; and garden furniture.

Characteristics

The KPOL® is specially developed for injection molded articles for general purpose applications. This product exhibits excellent processability with good melt strength and stiffness/impact strength balance.

It gives consistent processability and high gloss at the products.

It is a controlled rheology grade and High Crystallinity.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Controlled Rheology Food Contact Acceptable Good Impact Resistance Good Melt Strength Good Processability Good Stiffness High Gloss Highly Crystalline Homopolymer Medium Flow Nucleated
Uses	Closures Furniture General Purpose Thin-walled Parts
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	8.5	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	95		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	38.0	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	6.5	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	1100	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	25	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded)	92.0	°C	ASTM D648
Vicat Softening Temperature	155	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
POPELEN A-354	Lotte Chemical Corporation	PP Impact Copolymer	POPELEN
Sup-tech P260	Shanghai Suptech Engineering Plastics Co. Ltd.	PP, Unspecified	Sup-tech
TOTAL Polystyrene Crystal 535B	TOTAL Refining & Chemicals	PS (GPPS)	TOTAL Polystyrene
ABSCOM® SF1355	Polymer Compounders Limited	ABS	ABSCOM®
Hifax ETA3104	LyondellBasell Industries	TPO (POE)	Hifax