Sinkral® B 532/E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Sinkral® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KFnsIa_Sinkral-B-532-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sinkral B 532/E is an extrusion grade, which combines high toughness with good rigidity. Its rheological characteristics and good thermal stability are required for the production of large extruded sheet. Designation: Thermoplastics ISO 2580-ABS 1,EGN,105-04-25-20 Large sheet with good surface finish (co-extruded or not and suitable for high draw ratios) for a variety if uses in sectors such as refrigeration, sanitary, automotive, packaging and furniture (profiles). Grade available in natural color only. The composition of this grade, on request, can meet European Regulations for packaging in contact with foodstuffs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 45 | % | ASTM D638 |
| Flexural Modulus 3 | 2300 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | DIN 53453 |
| Charpy Unnotched Impact Strength | DIN 53453 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -40°C, 3.20 mm | 130 | J/m | ISO 180/4A |
| -20°C, 3.20 mm | 150 | J/m | ISO 180/4A |
| 0°C, 3.20 mm | 190 | J/m | ISO 180/4A |
| 23°C, 3.20 mm | 280 | J/m | ISO 180/4A |
| -40°C 5 | 10 | kJ/m² | ISO 180/1A |
| 23°C 6 | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ISO 306/A120 |
| -- | 104 | °C | ISO 306/B120 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 kHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 kHz) | 0.015 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | Internal Method | |
| Glow Wire Ignition Temperature (3.00 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,EGN,105-04-25-20 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T BLUE 7174 MAC | Arkema | Nylon 11 | Rilsan® Fine Powders |
| Absylux® Unfilled | Westlake Plastics Company | ABS | Absylux® |
| Ablefilm 561K | Henkel Ablestik | Epoxy | Ablefilm |
| Desmopan® DP 9370AU | Covestro - PUR | TPU-Polyether | Desmopan® |
| OnFlex™ S KE 40A-3S1727 | PolyOne Corporation | TPE | OnFlex™ |