INSPIRE™ TF0808
| Category: | TPO , Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KFMEbh_INSPIRE-TF0808.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™ TF0808S(U) is a 5 % talc filled PP exhibiting high flow characteristics in combination with a high impact resistance and a high stiffness. It is particularly well suited for low wall thickness bumper skins. This grade is proposed in two versions:
Application areas:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 to 1.0 | % | ISO 294-4 |
| Shrinkage - Total | 1.0 to 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | > 400 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 4.0 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 4.0 | kJ/m² | |
| 23°C | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/A120 |
| CLTE - Flow | DIN 53752 | ||
| -30 to 25°C | 6.3E-5 | cm/cm/°C | |
| 25 to 80°C | 9.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF M-1 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| EVALENE® PP PRJ1501 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |
| Karina IVORY PVC COMPOUND 730D35/ 1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DE006ER compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Sylvin 8980-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |