KIBITON® Q-Resin PB-5903
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBITON® Q-Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KF808S_KIBITON-Q-Resin-PB-5903.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KIBITON® Q-Resin PB-5903 is a Styrene Butadiene Block Copolymer (SBC) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.02 | g/cm³ | ASTM D792 |
| 23°C | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield, 4.00 mm | 27.0 | MPa | ISO 527-2/50 |
| Break, 4.00 mm | 19.0 | MPa | ISO 527-2/50 |
| 3.18 mm 1 | 24.5 | MPa | ASTM D638 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 2.00 mm | 2.0 | % | |
| Break, 4.00 mm | 200 | % | |
| Flexural Modulus | |||
| 6.35 mm 2 | 1370 | MPa | ASTM D790 |
| 4.00 mm 3 | 1400 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 4 | 31.4 | MPa | ASTM D790 |
| 4.00 mm 5 | 36.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 72 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 6.35 mm | 29 | J/m | ASTM D256 |
| 23°C | 2.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.35 mm 6 | 71.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 71.0 to 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 87.0 | °C | ASTM D1525 7 |
| -- | 93.0 | °C | ISO 306/A50 |
| -- | 89.0 | °C | ISO 306/A120 |
| -- | 70.0 | °C | ISO 306/B50 |
| -- | 68.0 | °C | ISO 306/B120 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3180 µm) | 90.5 | % | ASTM D1003 |
| Haze (3180 µm) | 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 120°C/hr |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-7180 | Wanhua Chemical Group Co., Ltd. | PC+TPU | Wanthane® |
| WeatherPro™ SG | Spartech Plastics | ABS | WeatherPro™ |
| NaturePlast PHE 008 | NaturePlast | PHA | NaturePlast |
| Clariant Nylon 6/6 6601-L BK-09 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Kumho PPG 6515 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |