Toyolac® 930-355
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KEnYw3_Toyolac-930-355.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 930-355 is a Methyl Methacrylate / ABS (MABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| 23°C | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 102 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 40.0 | MPa | ASTM D638 |
| 23°C | 45.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 40 | % | ASTM D638 |
| Break, 23°C | 16 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1810 | MPa | ASTM D790 |
| 23°C | 1830 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 61.0 | MPa | ASTM D790 |
| 23°C | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 190 | J/m | |
| 23°C, 12.7 mm | 150 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 74.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 85.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 85.0 | % | ISO 13468 |
| Haze (3000 µm) | 3.0 | % | ISO 14782 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hyundai EP PA6 LS910 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LNP™ LUBRICOMP™ RCL26 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Petrothene® NA420 | LyondellBasell Industries | LDPE | Petrothene® |
| POLIMAXX 2363LC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| NORYL™ WCD815U resin | SABIC Innovative Plastics Asia Pacific | PPE+TPE | NORYL™ |