EPO-TEK® T7109
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KDrCcg_EPO-TEK-T7109.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® T7109 is a two component, thermally conductive epoxy designed for die attach and heat-sinking applications found in the semiconductor, hybrid, medical and optical industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 377 | °C | TGA |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 1.78 | GPa | |
| Thixotropic Index | 1.79 | ||
| Weight Loss on Heating | |||
| 200°C | 0.020 | % | |
| 250°C | 0.25 | % | |
| 300°C | 0.98 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 45.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.6E-5 | cm/cm/°C | |
| -- 3 | 2.4E-4 | cm/cm/°C | |
| Thermal Conductivity | |||
| -- 4 | 0.70 | W/m/K | |
| -- 5 | 1.5 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 6 | Amber | ||
| -- 7 | White | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.33 | g/cm³ | |
| Viscosity 8(23°C) | 14 to 20 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 240 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.50 | ||
| Volume Resistivity (23°C) | > 8.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 4.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 40 mil |
| 5 . | 3 mil |
| 6 . | Part B |
| 7 . | Part A |
| 8 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven J-800 | Propilven, S.A. | PP Homopolymer | Propilven |
| Sinvicomp DBS3613 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| ExxonMobil™ PP8013L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Hanwha Total PP BJ550 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| ESTOPLAST EP 2050BB21 | Ester Industries Ltd. | PBT+PET | ESTOPLAST EP |