En Chuan 601
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | En Chuan Chemical Industries Co,. Ltd. |
| Trademark: | En Chuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KBL1KS_En-Chuan-601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is a low viscosity Bisphenol-A epoxy vinyl ester resin. It shows excellent mechanical properties and easy processing. It provides excellent corrosion resistance to a wide range of acids, alkalis and salt solutions. It is especially well suited for use in fabricating tanks, pipe and process equipment, most commercial FRP fabrication processes and anti-corrosion tank linings and coatings. This resin has obtained the DNV Type Approval Certificate. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Barcol Hardness 1 | 41 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | ASTM D790 | ||
| -- 2 | 3500 | MPa | ASTM D790 |
| -- 3 | 7500 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- 4 | 135 | MPa | ASTM D790 |
| -- 5 | 186 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 6(1.8 MPa, Unannealed) | 103 | °C | ASTM D648 |
| Additional Information |
|---|
| Red Accelerator, CO-oct (CO 6%): .4%Hardener, MEKPO (PO content, 55%): 1.6% |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (25°C) | 1.04 - 1.06 | g/cm³ | |
| Viscosity (25°C) | 0.20 - 0.70 | Pa·s | |
| Gel Time (25°C) | 20 - 30 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Modulus | |||
| -- 7 | 3250 | MPa | |
| -- 8 | 9510 | MPa | |
| Tensile Strength | |||
| -- 9 | 90.2 | MPa | |
| -- 10 | 118 | MPa | |
| Tensile Elongation at Break | |||
| -- 11 | 2.0 | % | |
| -- 12 | 4.4 | % |
| Note Message | |
|---|---|
| 1 . | Barcol 934-1 , Unfilled |
| 2 . | Unfilled |
| 3 . | Filled |
| 4 . | Unfilled |
| 5 . | Filled |
| 6 . | Unfilled |
| 7 . | Unfilled |
| 8 . | Filled |
| 9 . | Unfilled |
| 10 . | Filled |
| 11 . | Filled |
| 12 . | Unfilled |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAPPO™ JF1 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| VALOX™ V3504 resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |
| ADDILENE H 442 M30 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Bergamid™ A70 G30 Natural | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Hyundai EP PPF HT121 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |