LNP™ STAT-KON™ MD000AP compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KAeaYq_LNP-STAT-KON-MD000AP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing. Also known as: LNP* STAT-KON* Compound MD000AP Product reorder name: MD000AP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.4 | % | |
| Across Flow : 24 hr | 1.6 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1990 | MPa | ASTM D638 |
| -- | 1780 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 24.0 | MPa | ASTM D638 |
| Break | 22.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 1570 | MPa | ASTM D790 |
| -- 5 | 1670 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 39.7 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 39.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 33 | J/m | ASTM D256 |
| 23°C 7 | 3.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 680 | J/m | ASTM D4812 |
| 23°C 8 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 15.0 | J | ASTM D3763 |
| -- | 11.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 109 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 88.9 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 58.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aarolene® ARPE LD 300-1 | Aaron Industries Corp. | LDPE | Aarolene® |
| Clariant Nylon 6 60G33-L | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| LNP™ THERMOCOMP™ DC006ERH compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Sylvin 8299-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| StarFlex® 7393-1002 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |