LNP™ LUBRICOMP™ OFL36A compound
| Category: | PPS , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K9VBUi_LNPLUBRICOMPOFL36Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP OFL36A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound OFL-4036 Product reorder name: OFL36A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.30 - 0.48 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.13 - 0.18 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12300 | MPa | ASTM D638 |
| -- | 11100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 145 | MPa | ASTM D638 |
| Fracture | 124 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.7 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 197 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.44 | ASTM D3702 Modified | |
| With Self-Static | 0.35 | ASTM D3702 Modified | |
| Wear Factor - Washer | 33.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 9.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 3 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.40 | J | ASTM D3763 |
| -- | 1.97 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 269 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 266 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP CESTIDUR® PE-UHMW | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| NEXT REGRIND POMH 100P-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Homopolymer | NEXT REGRIND |
| ALTECH® PP-H A 1000/100 DS | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Lifoflex® UV 90 GC 1090 | ELASTO | SEBS | Lifoflex® |
| Polene LDPE JJ 4324 | TPI Polene Public Company Limited | LDPE | Polene LDPE |