Polymer-E H0105
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Asia Polymer Corporation (APC) |
| Trademark: | Polymer-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K8kqSr_Polymer-E-H0105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polymer-E H0105 is a Low Density Polyethylene product. It is available in Asia Pacific. Applications of Polymer-E H0105 include agricultural, bags/liners, construction applications and film. Primary characteristic: antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | < 0.55 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Blown Film | 196 | MPa | |
| 1% Secant, TD : 32 µm, Blown Film | 216 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 25.5 | MPa | |
| TD : Break, 32 µm, Blown Film | 21.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 330 | % | |
| TD : Break, 32 µm, Blown Film | 500 | % | |
| Dart Drop Impact (32 µm, Blown Film) | 300 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 31.8 µm | 51.0 | kN/m | |
| TD : 31.8 µm | 73.5 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 52.0 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 |
| Melting Temperature | 108 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°, 31.8 µm, Blown Film) | 75 | ASTM D523 | |
| Haze (31.8 µm, Blown Film) | 10 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PRC25UF0C-Black | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Nylene® PAC6-135 | Custom Resins Group | Nylon 66/6 | Nylene® |
| AIE PC/ABS A2200FR-3070 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| Lifoflex® GA 1020 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| Petrothene® GS707061 | LyondellBasell Industries | LLDPE | Petrothene® |