Toyolac® PX10-X06
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K8YYVc_Toyolac-PX10-X06-79441.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® PX10-X06 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 | g/cm³ | ASTM D792 |
| 23°C | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 114 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 54.0 | MPa | ASTM D638 |
| 23°C | 59.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 50 | % | ASTM D638 |
| Break, 23°C | 50 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2090 | MPa | ASTM D790 |
| 23°C | 2140 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.0 | MPa | ASTM D790 |
| 23°C | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 48 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 600 | J/m | |
| 23°C, 12.7 mm | 490 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 116 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9950C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 506 HB | RTP Company | SAN | RTP |
| ETILINAS HD5301AA | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| Exxtral™ Performance Polyolefin CNU017 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Polygen ASG6C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |