Pro-fax SC204
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K7SghM_Pro-fax-SC204.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax SC204 impact polypropylene copolymer is available in pellet form. This resin is typically used in thermoforming and sheet extrusion applications and offers excellent stiffness and good antistatic properties. For regulatory compliance information see Pro-fax SC204 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 8.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1590 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 113 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylfor® 74S5501PO 0001 | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Di-Pak™ E-4901-2 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| LNP™ STAT-KON™ CX99000 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ STAT-KON™ |
| Sumikon® X6952 | SBHPP | Phenolic | Sumikon® |
| Sylvin 9812-75 Red 6298 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |