Order Products : sales@su-jiao.com
Tritan™ FX100
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K6RYT0_Tritan-FX100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ FX100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Films manufactured from this new-generation copolyester can be thermoformed without pre-drying and with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan™ FX100 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Eastman Tritan™ FX100 copolyester is certified to NSF/ANSI Standard 51 for Food Equipment Materials. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr, 0.250 mm) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (23°C) 1 | 23haze | % | ASTM D1044 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C, 254.0 µm) 2 | 150 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| Elmendorf Tear Strength | |||
| MD : 23°C, 250.0 µm | 5 | N | ASTM D1922 |
| TD : 23°C, 250.0 µm | 6 | N | |
| PPT Tear Resistance | ASTM D2582 | ||
| MD : 23°C, 250.0 µm | 42 | N | |
| TD : 23°C, 250.0 µm | 56 | N | |
| Tear Propagation Resistance 3 | ASTM D1938 | ||
| MD : 23°C, 250.0 µm | 410 | gf | |
| TD : 23°C, 250.0 µm | 310 | gf |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance (250.0 µm) 4 | 89 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Energy | ASTM D5946 | ||
| Dispersive : 23°C, 250.0 µm | 39 | dyne/cm | |
| Polar : 23°C, 250 mm | 8 | dyne/cm | |
| Total : 23°C, 250.0 µm | 46 | dyne/cm |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 250 | µm | |
| Film Puncture Energy 5(250 µm) | 4.60 | J | ASTM D3763 |
| Secant Modulus | ASTM D882 | ||
| MD : 250 µm | 1500 | MPa | |
| TD : 250 µm | 1400 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 250 µm | 41.0 | MPa | |
| TD : Yield, 250 µm | 40.0 | MPa | |
| MD : Break, 250 µm | 59.0 | MPa | |
| TD : Break, 250 µm | 52.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 250 µm | 7.0 | % | |
| TD : Yield, 250 µm | 7.0 | % | |
| MD : Break, 250 µm | 180 | % | |
| TD : Break | 200 | % | |
| Dart Drop Impact 6 | ASTM D1709A | ||
| -30°C, 250 µm | 910 | g | |
| 23°C, 250 µm | 880 | g | |
| Trouser Tear Resistance 7 | ISO 6383-1 | ||
| MD : 250 µm | 11.0 | N/mm | |
| TD : 250 µm | 11.0 | N/mm | |
| Oxygen Permeability (23°C, 250 µm, 50% RH) | 32 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 23°C, 100% RH, 250 µm | 4.0 | g/m²/24 hr | |
| 38°C, 100% RH, 250 µm | 11 | g/m²/24 hr |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1938 | ||
| Split 8 | 12 | kN/m | |
| Split 9 | 13 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 110 | °C | |
| CLTE - Flow (23°C, 0.250 mm) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | DSC | ||
| 60°C | 1700 | J/kg/°C | |
| 100°C | 1900 | J/kg/°C | |
| 150°C | 2200 | J/kg/°C | |
| 200°C | 2400 | J/kg/°C | |
| 250°C | 2600 | J/kg/°C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 250 µm) | 161 | ASTM D2457 | |
| Refractive Index | 1.550 | ASTM D542 | |
| Transmittance (250 µm) | 92.0 | % | ASTM D1003 |
| Haze (250 µm) | 0.70 | % | ASTM D1003 |
| Yellowness Index (250 mm) | 0.50 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | average at 25 cycles |
| 2 . | 50% RH |
| 3 . | 254 mm/min |
| 4 . | % Transmission at 380 nm |
| 5 . | Dynatup, Total Energy |
| 6 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 7 . | 200 mm/min |
| 8 . | TD, 250 µm |
| 9 . | MD, 250 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Clariant Nylon 6/12 612-01-L | Clariant Corporation | Nylon 612 | Clariant Nylon 6/12 |
| DJSilicone NE-8161 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Karina BLACK PVC COMPOUND 900-DA-48/ 1-C-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1500-0871 | LEHVOSS Group | PSU | LUVOCOM® |