Borealis PP BA110CF

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	Borealis AG
Trademark:	Borealis PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	K5tNBm_Borealis-PP-BA110CF.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
BA110CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented film on blown film lines.

General Information
Features	Copolymer Good Heat Seal Good Impact Resistance Good Toughness Low Gel Low Temperature Impact Resistance Med.-Wide Molecular Weight Distrib.
Uses	Film Food Packaging Laminates Non-oriented Film Oriented Film Stationary Supplies
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Blown Film Coextrusion

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	0.85	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus (23°C, Injection Molded)	1200	MPa	ISO 178

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Tensile Modulus			ISO 527-3
MD : 50 µm	500	MPa
TD : 50 µm	600	MPa
Tensile Strength			ISO 527-3
MD : 50 µm	40.0 to 60.0	MPa
TD : 50 µm	30.0 to 50.0	MPa
Tensile Elongation			ISO 527-3
MD : Break, 50 µm	550	%
TD : Break, 50 µm	750	%
Instrumented Dart Impact (50 µm, Total Energy)	25.0	J	ISO 7765-2

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	166	°C	ISO 3146

Optical	Nominal Value	Unit	Test Method
Gloss (50.0 µm)	> 3		ASTM D2457
Haze (50.0 µm)	< 40	%	ASTM D1003

Resin Grade	Manufacturer	Category	Trademark
Torlon® AI-10 LM	Solvay Specialty Polymers	PAI	Torlon®
XANTAR® 24 UR	Mitsubishi Engineering-Plastics Corp	PC	XANTAR®
Flexalloy® 9300-65	Teknor Apex Company	PVC Elastomer	Flexalloy®
Sylvin 83028-90 Green 3195	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LNP™ THERMOCOMP™ Lexan_LGK5030 compound	SABIC Innovative Plastics Asia Pacific	PC	LNP™ THERMOCOMP™