SABIC® HDPE M40053S
| Category: | HDPE , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K4w5ob_SABICHDPEM40053S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
M40053S is UV stabilized High Density Polyethylene grade with narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good balance of stiffness and impact at low temperatures and is also having good weatherability and surface properties. M40053S is specially developed for high demanding dust bin market, shipping containers for low temperature storage, industrial pails etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693B | ||
| 10% Igepal, molded, F50 | 4.00 | hr | ASTM D1693B |
| 100% Igepal, molded, F50 | 7.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Injection Molded) | 900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, injection molding | 23.0 | MPa | ASTM D638 |
| Fracture, injection molding | 21.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Injection Molded) | > 800 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 800 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 21.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 - 260 | °C | |
| Middle Temperature | 232 - 260 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Mold Temperature | 15.0 - 60.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1371 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| K-vinyl 60 Deg C Rating Insulation (80-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Jiangsu Sinarise EX8535X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| LG PVC LS300 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| Karina YELLOW PVC COMPOUND 804-02/ 69-Y-RTC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |