Order Products : sales@su-jiao.com
Impet® 2700 GV1/45 (Europe)
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Impet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K3kBNY_Impet-2700-GV1-45-Europe-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyethylene terephthalate, 45% glass filled, high flowability, excellent gloss, high modulus, very high heat deflection temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 185 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 31 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 252 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 228 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 170 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 260 | °C | ISO 306/B50 |
| Melting Temperature 1 | 248 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 5.20 | IEC 60250 | |
| 1 MHz | 4.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | IEC 60250 | |
| 1 MHz | 0.017 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 135 - 145 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 - 2.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 270 to 290°CZone 4 Temperature: 280 to 290°CFeed Temperature: 40 to 60°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 C MS | RTP Company | Nylon 11 | RTP |
| NORYL™ WCP841 resin | SABIC Innovative Plastics Asia Pacific | PPE+TPE | NORYL™ |
| Fainplast PVC PH 50/1 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| NILAMID® XS3 CF30 TF15 | Nilit Plastics | Nylon, Unspecified | NILAMID® |
| CYCOLOY™ CX7211 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |