POLYfill PPH TS15010
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K3enx7_POLYfill-PPH-TS15010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 to 1.6 | % | |
| Flow | 1.3 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1700 | MPa | ISO 178 |
| Flexural Stress | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 104 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/A50 |
| -- | 82.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 A | RTP Company | Nylon 6 | RTP |
| RTP 1601 | RTP Company | PAS | RTP |
| Geon™ Vinyl Flexible R9788A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ THERMOCOMP™ AF001H compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| LUVOCOM® 1-8068/GY VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |