PlexTuf 2000
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | PlexTuf |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K3VSeL_PlexTuf-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PlexTuf 2000 is a Polymethyl Methacrylate Acrylic product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1520 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 37.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 101 | °C | |
| 1.8 MPa, Annealed | 87.8 | °C | |
| Vicat Softening Temperature | |||
| -- | 92.2 | °C | ASTM D1525 2 |
| -- | 85.0 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 91.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 2.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA Unspecified | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealed 4 hrs at 80°C |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4760 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Adell Polyamide AL-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| INSTRUC PA66IM | Infinity LTL Engineered Compounds | Nylon 66 | INSTRUC |
| Lion Idemitsu Composites PPS V170N3 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Sumiliteresin® PR-50641 | SBHPP | Phenolic | Sumiliteresin® |