BJB Epoxy TC-1600 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K3PevL_BJB-Epoxy-TC-1600-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-1600 A/B is an unfilled, low viscosity laminating resin generally used for fabricating reinforced laminates. It features an ability to cure at room temperature for applications that do not require a working service temperature above 180°F (82°C). This system can provide service up to 300°F (149°C) when post-cured. TC-1600 is commonly used to reinforce fiberglass, Kevlar/aramid, and carbon fiber fabrics. It is also used as an adhesive for bonding wood, composites, and other substrates. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for fillets, fairings, and bonding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A : 25°C | 1.147 | g/cm³ | |
| Part B : 25°C | 0.978 | g/cm³ | |
| Water Absorption - 100 hr | 1.5 | % | ASTM D570 |
| Shrinkage | 0.015 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time (25°C) | 12.0 to 15.0 | hr | |
| Work Time (25°C) 1 | 30.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | 1.70 | Pa·s | |
| Part A : 25°C | 2.00 | Pa·s | |
| Part B : 25°C | 0.185 | Pa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 241 | MPa | ASTM D638 |
| Flexural Modulus | 15900 | MPa | ASTM D790 |
| Flexural Strength | 276 | MPa | ASTM D790 |
| Compressive Strength | 290 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 121 | °C | ASTM D648 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D3386 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 20 | ||
| Post Cure Time | 12 to 15 | hr |
| Note Message | |
|---|---|
| 1 . | 1 lb mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ 180 Series 186A | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 180 Series |
| Karina BLUE PVC COMPOUND 802-06/795-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND 909D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniCarb™ PC/PBT 1020 FR0 | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |
| Pibiflex® E4482 NATURALE | SO.F.TER. SPA | TPC-ET | Pibiflex® |