Lucon® PN9009
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K3Lmow_Lucon-PN9009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Thermal Conductivity, Chemical Resistance, High Heat Resistance Application Electrical or Electronic Parts (Heat Sink, LED), Motor Housing |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (320°C/5.0 kg) | 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Flexural Modulus 2(6.40 mm) | 13700 | MPa | ASTM D790 |
| Flexural Strength 3(Yield, 6.40 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 260 | °C | ASTM D648 |
| Thermal Conductivity | 2.5 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+10 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 310 to 320 | °C | |
| Front Temperature | 320 to 325 | °C | |
| Nozzle Temperature | 310 to 330 | °C | |
| Processing (Melt) Temp | 330 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 31T1010 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Radilon® BGV HZ 30 Natural | Radici Plastics | Nylon 6 | Radilon® |
| TABOND 3021 | SILON s.ro | LLDPE | TABOND |
| FERREX® GPP40CC90UL | Ferro Corporation | PP Homopolymer | FERREX® |
| PLUSTEK PA325G5 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |