LUVOCOM® 50-8907 Datasheet,PC,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®50-8907 is a polycarbonate (PC) material, and the filler is glass fiber reinforced material. This product is available in Europe,. LUVOCOM®The main features of 50-8907 are: flame retardant/rated flame sterilizable Good dimensional stability Good stiffness Wear-resistant Typical application areas include: Electrical/electronic applications Reflector engineering/industrial accessories Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass fiber reinforced material
Additive	PTFE lubricant
Features	Good dimensional stability Low friction coefficient Rigid, good Good disinfection Good strength Good wear resistance Lubrication
Uses	Reflector Engineering accessories Switch Application in Automobile Field Business equipment Medical/nursing supplies
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.36	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.15	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	6500	MPa	ISO 527-2
Tensile Stress (Break)	115	MPa	ISO 527-2
Tensile Strain (Yield)	3.0	%	ISO 527-2
Flexural Modulus	5500	MPa	ISO 178
Flexural Stress	165	MPa	ISO 178
Coefficient of Friction
Dynamic	0.23
Static	0.17
Flexural Strain at Flexural Strength	3.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	170	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength
-30°C	46	kJ/m²	ISO 179/1fU
23°C	50	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	175	°C	ISO 75-2/A
Continuous Use Temperature	150	°C	UL 746B
Vicat Softening Temperature	180	°C	ISO 306/A

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	130	°C
Drying Time	2.0 - 4.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	310 - 330	°C
Middle Temperature	320 - 340	°C
Front Temperature	330 - 350	°C
Nozzle Temperature	320 - 340	°C
Processing (Melt) Temp	330	°C
Mold Temperature	80.0 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PC , Polycarbonate
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	K37GrG_LUVOCOM-50-8907.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POWERSIL® 3500	Wacker Chemie AG	Silicone	POWERSIL®
Ecomass® 706BI76	Ecomass Technologies	ABS	Ecomass®
Hanwha Total PP TB52L	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP
Jackdaw PP ER38BK6306	Jackdaw Polymers	PP Homopolymer	Jackdaw PP
KEBAFORM® C 8027	BARLOG plastics GmbH	Acetal (POM) Copolymer	KEBAFORM® C