Infino FD-1106
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K2dvWe_InfinoFD1106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino FD-1106 is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: lighting equipment. The main features are: flame retardant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.45 - 0.55 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.45 - 0.55 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.45 - 0.55 | % | ISO 2577 |
| Traffic : 3.20mm | 0.45 - 0.55 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 115 | ASTM D785 | |
| R scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1890 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 6.20 | MPa | ISO 527-2/50 |
| Fracture 3 | 62.0 | MPa | ASTM D638 |
| Fracture | 6.20 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 120 | % | ASTM D638 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| -- | 2100 | MPa | ASTM D790 |
| -- | 2140 | MPa | ISO 178 |
| Flexural Strength 6 | 84.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 131 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 131 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | |||
| 1000 µm | 47.8 | % | ASTM D1003 |
| 1000 µm | 47.8 | % | ISO 13468 |
| Haze | |||
| 1000 µm | 96 | % | ASTM D1003 |
| 1000 µm | 96 | % | ISO 13468 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Diffusion Degree (1.00 mm) | 55 | °C | Internal method |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4mm |
| 8 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® GF8001 | Covestro - Polycarbonates | PC | Makrolon® |
| POLYshine PBT D201 FB52 | Polykemi AB | PBT | POLYshine |
| XENOY™ 5220U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| Dynaflex™ G7630-9 (Black) | PolyOne Corporation | TPE | Dynaflex™ |
| LNP™ STAT-KON™ AE002 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-KON™ |