SABIC® LLDPE 6821WE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K2TmSm_SABIC-LLDPE-6821WE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® LLDPE 6821WE is a hexene-linear low density polyethylene. Films made from this resin exhibit outstanding tensile strength, stiffness, dart drop, impact strength, tear strength and hottack properties. This material contains a high amount of anti block and slip erucamide. The suffix E denotes European origin. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 50 µm | 220 | MPa | ASTM D882 |
| TD : 50 µm | 250 | MPa | ASTM D882 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 12.5 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 14.0 | MPa | ISO 527-3 |
| MD : 50 µm | 35.0 | MPa | ISO 527-3 |
| TD : 50 µm | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 520 | % | ISO 527-3 |
| TD : Break, 50 µm | 650 | % | ISO 527-3 |
| Total Energy Impact (50 µm) | 1.50 | J | ASTM D4272 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 50 µm | 3.5 | N | ISO 6383-2 |
| TD : 50 µm | 18 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 111 | °C | ISO 306/A |
| Melting Temperature | 125 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 45 | ASTM D2457 | |
| Haze | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| The value Haze, ASTM D1003, was tested in a HazemeterClarity, SABIC Method: 20 mVPuncture Resistance, SABIC Method: 450 J/mBlocking, SABIC Method: 10 gRe-blocking, SABIC Method: <10 gKiefel IBC: 140 kg/hDie Size: 200 mmDie Gap: 2.7 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2948-85 White 1516 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Niretan B 27 M AE/V2 | Soredi S.p.a. | Nylon 6 | Niretan B |
| EVICOM™ EX6/855 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| ICORENE® 3660 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |
| Karina NATURAL PVC COMPOUND V-150 LT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |