LNP™ THERMOCOMP™ Noryl_PCN2910 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K2RANp_LNP-THERMOCOMP-Noryl-PCN2910-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* Noryl_PCN2910 compound is a 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11400 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 123 | MPa | ASTM D638 |
| Yield | 106 | MPa | ISO 527-2/5 |
| Break 3 | 123 | MPa | ASTM D638 |
| Break | 106 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.5 | % | ASTM D638 |
| Yield | 1.3 | % | ISO 527-2/5 |
| Break 5 | 1.5 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9790 | MPa | ASTM D790 |
| 100 mm Span 7 | 8760 | MPa | ASTM D790 |
| -- 8 | 9130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Break, 50.0 mm Span 9 | 165 | MPa | ASTM D790 |
| Break, 100 mm Span 10 | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 11(23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 12 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 13 | 14 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 7.12 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 123 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 129 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 141 | °C | ASTM D1525 15 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.7E-5 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| 2.29 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Nozzle Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2.6 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6890 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SABIC® Vestolen A 6060R 65306 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Toyolac® 335-X01 | Toray Resin Company | ABS | Toyolac® |
| ACCUGUARD™ CP0467V0CSL | ACLO Compounders Inc. | PP Copolymer | ACCUGUARD™ |
| LNP™ COLORCOMP™ J1000R compound | SABIC Innovative Plastics Europe | PESU | LNP™ COLORCOMP™ |