LNP鈩?VERTON鈩?RV0079 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K2KXZV_LNP-VERTON-RV0079-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* RV0079 is a compound based on Nylon 66 resin containing 35% Long Glasss Fiber. Added features of this material include: Flame Retardant, Structural. Also known as: LNP* VERTON* Compound RF-7007 FR Product reorder name: RV0079 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.59 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.75 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14800 | MPa | ASTM D638 |
| -- | 12400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 194 | MPa | ASTM D638 |
| Yield | 177 | MPa | ISO 527-2/5 |
| Break 3 | 194 | MPa | ASTM D638 |
| Break | 177 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.8 | % | ASTM D638 |
| Yield | 1.7 | % | ISO 527-2/5 |
| Break 5 | 1.8 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9700 | MPa | ASTM D790 |
| -- 7 | 10800 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 241 | MPa | |
| Break, 50.0 mm Span | 241 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 310 | J/m | ASTM D256 |
| 23°C 9 | 36 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 810 | J/m | ASTM D4812 |
| 23°C 10 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.5 | J | ASTM D3763 |
| -- | 5.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 254 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 255 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.70 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORDEL™ IP 4785HM | The Dow Chemical Company | EPDM | NORDEL™ |
| AKROMID® B3 2 RM-D natural (3390) | AKRO-PLASTIC GmbH | Nylon 6+ABS | AKROMID® |
| LUVOCOM® 19-7276 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| POLYFLAM® RIPP 490 E CS1 | A. Schulman Europe | PP Copolymer | POLYFLAM® |
| Hostacom PPU X9067HS 104908 | LyondellBasell Industries | PP Copolymer | Hostacom |