Equinox® 38 Medium
| Category: | Silicone , Silicone |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Equinox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K27ZPq_Equinox-38-Medium.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Equinox® Silicone Putty Products are new silicone compounds (platinum catalyst) that can be easily mixed and applied by hand to a variety of surfaces. Equinox® Putty is mixed in equal amounts (1A:1B) by volume. Equinox® 35 has a pot life of about 1 minute with a cure time of about 7 minutes at room temperature (73°F/23°C). Equinox® 38 has a pot life of 4 minutes with a cure time of 30 minutes and Equinox® 40 is a slower version with a 30 minute pot life and 5 hour demold time. Shrinkage is low and cured rubber is exceptionally strong (very high tensile strength), durable and will resist high temperatures (for casting low-temperature melt metal alloys). They also resist cure inhibition. Equinox® Silicones are also FOOD SAFE and can be used for culinary applications. (See separate technical bulletin for usage instructions available at www.smooth-on.com). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.768 | cm³/g | ASTM D1475 |
| Viscosity | Putty | ASTM D2393 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume or weight |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.030 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 38 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.820 | MPa | ASTM D412 |
| Tensile Strength (Break) | 3.59 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 430 | % | ASTM D412 |
| Tear Strength 1 | 24.5 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life | 4.0 | min | ASTM D2471 |
| Demold Time | 30 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 8211-35 | ExxonMobil Chemical | TPV | Santoprene™ |
| TAROPRENE® 1 D50 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| WanBlend® WHT-1170M | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| EVAL™ F171 | Kuraray Co., Ltd. | EVOH | EVAL™ |
| Gallonprene® GP320-75 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |