Trilene® HY3.8FY
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Trilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K1VbrX_Trilene-HY3-8FY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trilene HY3.8FY is a polypropylene homopolymer for production of stretched tape (yarn or raffia). Also can be use for transparent woven bag which require good clarity, stiffness. This grade uses Unipol® polypropylene technology with latest catalyst technology. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.903 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1290 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 3 |
| Peak Melting Temperature 4 | 163 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 - 250 | °C |
| Extrusion instructions |
|---|
| Water Bath Temperature: 27 to 35°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 标准 B (120°C/h) |
| 4 . | 10°C/min, 2nd heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 HS TFE 15 | RTP Company | Nylon 66 | RTP |
| Quadrant EPP Symalit PVDF 1000 | Quadrant Engineering Plastic Products | PVDF | Quadrant EPP |
| TOTAL Polyethylene Lumicene® M 2704 EP | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| NatureFlex™ 165NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| CYCOLAC™ MG38U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |