Next Nylon 66 Prime Series PXH-01NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K1EGGU_Next-Nylon-66-Prime-Series-PXH-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 UnFilled Natural Compound Product Applications Typical application include fast processing high stress technical parts or electrically insulating parts. Benefits This grade has execellent flow and improved ambidient and low temperature toughness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.4 | -- | % | |
| Across Flow | 1.4 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.2 | -- | % | |
| Saturation 1 | 6.7 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 80 | -- | ||
| R-Scale | 115 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 85.0 | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | > 50 | % | ASTM D638 |
| Flexural Modulus | 3200 | 2900 | MPa | ASTM D790 |
| Flexural Strength | 120 | 85.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | 88 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 200 | -- | °C | |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | |
| Melting Temperature | 260 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 22 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 275 | °C | |
| Front Temperature | 275 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SINOF DH-F22E-1 | SINOF HI-TECH MATERIAL CO. LTD | PVDF | SINOF |
| Moplen EP642R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| TEREZ PC/ASA Blend 1000 | TER HELL PLASTIC GMBH | ASA+PC | TEREZ PC/ASA |
| NEOFLON™ EFEP RP-5000AS | DAIKIN AMERICA, INC. | Fluoropolymer | NEOFLON™ |
| Clariant Nylon 6/6 PA-133G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |