Retpol® 9010 HS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K19ERg_Retpol-9010-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epalex PDR 7380/2 UV3 is a thermoplastic rubber modified polypropylene compound. It is a low flow injection moulding grade developed for excellent impact strength to -40°C and below. The higher level of rubber modification provides for parts with greater flexibility and a lower surface hardness. It has been stabilized against degradation from continuous outdoor exposure. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 170 | % | ASTM D638 |
| Flexural Modulus | 1220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 899 X 131271 A | RTP Company | Acetal (POM) Copolymer | RTP |
| Badamid® C70 FR HF | Bada AG | Nylon 66/6 | Badamid® |
| Akulon® K223-P2 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| CYCOLOY™ XCY620S resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| XANTAR® C CM 526 | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |