TRIBOCOMP® PA6 TS13
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K0sT6Y_TRIBOCOMP-PA6-TS13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PA6 TS13 is a Polyamide 6 (Nylon 6) product. It is available in Europe. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.2 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 60.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | > 10 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 8.0E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.24 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 29 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 220 to 260 | °C | |
| Middle Temperature | 225 to 270 | °C | |
| Front Temperature | 230 to 280 | °C | |
| Nozzle Temperature | 230 to 290 | °C | |
| Processing (Melt) Temp | < 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP270 | Kolon Plastics, Inc. | PBT | SPESIN® |
| Sumitomo PE FS253S | Sumitomo Chemical Asia | LLDPE | Sumitomo PE |
| Moplen APD369 | LyondellBasell Industries | PP Random Copolymer | Moplen |
| DJSilicone NE-9130 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Glastic® 1603-2A | Glastic Corporation | Polyester, TS | Glastic® |