Braskem PP H 603
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K0rW0N_Braskem-PP-H-603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: H 603 is a low melt flow rate homopolymer with general purpose additive package. This resin is designed for blow moulding and extrusion. H 603 exhibits an excellent processability, excellent stiffness/impact strength balance, high melt strength and low odor/taste transfer Applications: Bottles for mineral water, vinegar and food; Flat and corrugated sheets in general |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 98 | ASTM D785 | |
| R-Scale | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 33.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 14 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1350 | MPa | ASTM D790 |
| Injection Molded | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, Injection Molded | 45 | J/m | ASTM D256 |
| 23°C, Injection Molded | 3.8 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 89.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 89.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 53.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 154 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COSMOPLENE® FC9411G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| Diaterm® B26 GF25 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 66 | Diaterm® |
| ENGAGE™ 8457 DA | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| Karina GRAY MBU -E 18/ 15-IE-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ MF002S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |