Infino XP-2140C
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K0ZNR7_Infino-XP-2140C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS/GF with 40% GF reinforcement that is applied to automobile parts etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 316°C/5.0 kg | 55 | g/10 min | ASTM D1238 |
| 316°C/5.0 kg | 83 | g/10 min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.27 to 0.33 | % | |
| Across Flow : 3.20 mm | 0.32 to 0.39 | % | |
| Ash Content | 40 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6900 | MPa | ASTM D638 |
| -- | 11400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 190 | MPa | ASTM D638 |
| Yield | 180 | MPa | ISO 527-2/50 |
| Break 3 | 180 | MPa | ASTM D638 |
| Break | 180 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 13000 | MPa | ASTM D790 |
| -- 6 | 13400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 260 | MPa | ASTM D790 |
| -- 8 | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 85 | J/m | ASTM D256 |
| 23°C 10 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 282 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 283 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 283 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 270 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 267 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 272 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Desiccant Dryer | 6.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 290 | °C | |
| Middle Temperature | 290 to 300 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Nozzle Temperature | 330 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Injection Pressure | 49.0 to 127 | MPa | |
| Back Pressure | 0.981 to 1.96 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven S-900 | Propilven, S.A. | PP Homopolymer | Propilven |
| SOLARENE G181 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Adell PP ER-39 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Gallonprene® GP520-4505 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ EXL1162T resin | SABIC Innovative Plastics | PC | LEXAN™ |