LNP™ THERMOCOMP™ AF001H compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ixu4R6_LNPTHERMOCOMPAF001Hcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP AF001H is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound AF-1001 HC Product reorder name: AF001H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2750 | MPa | ASTM D638 |
| Tensile Strength (Break) | 40.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 2740 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 266 - 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 40A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Baoding 6180 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Axiall PVC UV-6670 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Polygen SFG6C-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| LNP™ STAT-KON™ ME006 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |