Adsyl 7623 XCP
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ix3Aso_Adsyl7623XCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adsyl 7623 XCP is an advanced polyolefin, specially designed for use as a sealing or metallized layer in co-extruded film applications. This grade features a very low seal initiation temperature. It contains anti-block additives. For regulatory information please refer to Adsyl 7623 XCP Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, cast film | 280 | MPa | ISO 527-3/25 |
| TD : 50 µm, cast film | 280 | MPa | ISO 527-3/25 |
| Tensile Stress | ISO 527-3/500 | ||
| MD : yield, 50 µm, cast film | 14.0 | MPa | ISO 527-3/500 |
| TD : yield, 50 µm, cast film | 14.0 | MPa | ISO 527-3/500 |
| MD : fracture, 50 µm, casting film | 45.0 | MPa | ISO 527-3/500 |
| TD : fracture, 50 µm, casting film | 35.0 | MPa | ISO 527-3/500 |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : yield, 50 µm, cast film | 17 | % | ISO 527-3/500 |
| TD : yield, 50 µm, cast film | 15 | % | ISO 527-3/500 |
| MD : fracture, 50 µm, casting film | 900 | % | ISO 527-3/500 |
| TD : fracture, 50 µm, casting film | 800 | % | ISO 527-3/500 |
| Seal Initiation Temperature | 105 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 62.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 107 | °C | ISO 306/A50 |
| Melting Temperature | 132 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 87 | ASTM D2457 | |
| Haze (50.0 µm) | 1.2 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APICAL 300AV | Kaneka Corporation | Film, PI | APICAL |
| Clariant Nylon 6/6 PA-113TF20 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Flontech® FT-BRR40-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Estane® 58137 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Plaskon CMU-880-MA | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |