VENELENE® 11E1
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IvhI0a_VENELENE-11E1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Force (50 µm) | 5.49 | N | ASTM D3420 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm | 34.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 28.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 810 | % | ASTM D882 |
| TD : Break, 50 µm | 970 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 220 | g | ASTM D1922 |
| TD : 50 µm | 530 | g | ASTM D1922 |
| Impact Resistance, Film | 70.0 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 140 | MPa | ASTM D882 |
| TD | 150 | MPa | ASTM D882 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 260 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 0.7 - 1.0 mm. Pulling speed: < 250 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PE HDPE-2052 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Nylene® 9110 G33 | Custom Resins Group | Nylon 610 | Nylene® |
| Dutral® TER 6537 | Versalis S.p.A. | EPDM | Dutral® |
| KOPA® KN163HI | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| TECACOMP® PBT TC black 4207 | Ensinger GmbH | PBT | TECACOMP® |