| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IvLYpv_SABIC-HDPE-PCG863.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG863 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. It is an easy-to-process, stiff grade. Compliance to regulations. SABIC® HDPE PCG863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.963 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 8.0 | g/10 min | |
| 190°C/5.0 kg | 23 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 40.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1450 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 31.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 15.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1650 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 94.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| Melting Temperature (DSC) | 134 | °C | ISO 11357-3 |
| Enthalpy Change | 226 | J/g | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stirol UPS-0801 (extra) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| Xuchuan XCS-2063B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Niblan V100 AE/V0 | Soredi S.p.a. | PBT | Niblan |
| AKROMID® A4 5 EN natural (3162) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| POLYform C M90 K5 | Polykemi AB | Acetal (POM) Copolymer | POLYform C |