Generic PP, Unspecified - Glass\Mineral
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IvEYcs_Generic-PP-Unspecified---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 - 1.27 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 3.7 - 10 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 2.0 - 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.28 - 0.90 | % | ASTM D955 |
| Transverse flow : 23°C | 0.89 - 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 100 - 110 | ASTM D785 | |
| Durometer Hardness (23°C) | 74 - 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 27.6 - 93.9 | MPa | ASTM D638 |
| 23°C | 26.2 - 81.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.9 - 5.1 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 1610 - 6020 | MPa | ASTM D790 |
| 23°C | 2300 - 7320 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 51.5 - 127 | MPa | ASTM D790 |
| 23°C | 37.0 - 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 - 8.2 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 35 - 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 190 - 440 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 0.226 - 0.845 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 127 - 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 - 148 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 80.0 - 150 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 83.0 | °C | |
| Drying Time | 1.5 - 3.1 | hr | |
| Suggested Max Moisture | 0.048 - 0.053 | % | |
| Rear Temperature | 185 - 246 | °C | |
| Middle Temperature | 195 - 246 | °C | |
| Front Temperature | 205 - 246 | °C | |
| Nozzle Temperature | 215 - 232 | °C | |
| Processing (Melt) Temp | 210 - 239 | °C | |
| Mold Temperature | 37.6 - 50.6 | °C | |
| Injection Pressure | 6.55 - 85.9 | MPa | |
| Back Pressure | 0.345 - 1.44 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D223 GF15 FR | Polykemi AB | PBT | POLYshine |
| WELLAMID Nylon 6000 CF 18 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Zeoforte® ZSC2295L | Zeon Corporation | NBR | Zeoforte® |
| OTECH PVC OW132 - Wire Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| LNP™ STAT-KON™ KEP33 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |