Durethan® B 31 SK 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IvCaxq_DurethanB31SK000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, injection molding |
| General Information | |
|---|---|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.14 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 110 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Vertical flow direction : 280°C, 3.00mm 1 | 1.1 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 2 hours, 3.00mm 2 | 0.15 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 3.00mm 3 | 0.90 | -- | % | ISO 2577 |
| Flow direction : 120°C, 2 hours, 3.00mm 4 | 0.15 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 10 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 150 | 55.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 3200 | 1100 | MPa | ASTM D638 |
| 23°C | 3500 | 1100 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Yield, 23°C | 80.0 | 40.0 | MPa | ASTM D638 |
| Yield, 23°C | 85.0 | 50.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 50.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 20 | % | ASTM D638, ISO 527-2/50 |
| Fracture, 23°C | 35 | > 50 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 10 | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 900 | MPa | ISO 899-1 |
| 1000 hr | -- | 700 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 2700 | 703 | MPa | ASTM D790 |
| 23°C 6 | 3000 | 900 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 5.0% strain, 23°C | 115 | 35.0 | MPa | ASTM D790 |
| 3.5% strain 7 | 100 | 30.0 | MPa | ISO 178/A |
| 23°C 8 | 120 | 40.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 9(23°C) | 6.0 | 8.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 10(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 14-030, | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 11 | 70.0 | -- | J | ISO 6603-2 |
| -- 12 | 46.0 | -- | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 13 | 6810 | -- | N | ISO 6603-2 |
| -- 14 | 4650 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C, 3.18 mm | 59 | 750 | J/m | ASTM D256 |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 120 | -- | kJ/m² | ISO 180/1U |
| 23°C | 120 kJ/m² | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, not annealed, 3.99mm | 180 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed, 3.99mm | 60.0 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 50.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 15 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec (1.50 mm) | 105 | -- | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | -- | °C | UL 746 |
| RTI (1.50 mm) | 75.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 - 1.0E+15 | 1.0E+12 - 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 30 | 30 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 30 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 16 | 3.80 | 20.0 | IEC 60250 | |
| 23°C, 1 MHz 17 | 3.40 | 4.60 | IEC 60250 | |
| 23°C, 100 Hz | 4.00 | 13.0 | IEC 60250 | |
| 23°C, 1 MHz | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.050 | 2.3 | IEC 60250 | |
| 23°C, 100 Hz | 6.0E-3 | 0.19 | IEC 60250 | |
| 23°C, 1 MHz | 0.020 0.070 | 0.10 0.40 | IEC 60250 | |
| Comparative Tracking Index | ||||
| Solution a | 600 | -- | V | IEC 60112 |
| Solution B | 525 | -- | V | IEC 60112 |
| -- | -- | 600 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | V-2 | -- | UL 94 | |
| 1.60 mm | V-2 | -- | UL 94 | |
| 3.00 mm | V-2 | -- | UL 94 | |
| 3.20 mm | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 18 | 25 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 400 Bar |
| 2 . | 150x150x3 |
| 3 . | 150x150x3; MT 80°C; 400 Bar |
| 4 . | 150x150x3 |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Pull Rate: 2 mm/min; 50% RH |
| 10 . | US-FMVSS302 |
| 11 . | -30°C |
| 12 . | 23°C |
| 13 . | -30°C |
| 14 . | 23°C |
| 15 . | 10°C/min |
| 16 . | Tinfoil Electrodes |
| 17 . | Tinfoil Electrodes |
| 18 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 303 Z | RTP Company | PC | RTP |
| T-Blend® 6800N-AB | TSRC Corporation | TPE | T-Blend® |
| Chemiton CSF0NA 90 | Franplast S.r.l. | SEBS | Chemiton |
| Karina BLACK PVC COMPOUND -E 880-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Romiloy® 4010/02 UV GF8 | ROMIRA GmbH | ABS+Nylon | Romiloy® |