Exelene® HDPE 5100M
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Montachem International, Inc. |
| Trademark: | Exelene® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iuwndq_Exelene-HDPE-5100M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Characteristics:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | |
| 190°C/21.6 kg 1 | 10 | g/10 min | |
| Environmental Stress-Cracking Resistance | |||
| 50°C, 3.10 mm, 100% Igepal CO-630, F50 | > 600 | hr | ASTM D1693A |
| 50°C, 1.90 mm, 100% Igepal CO-630, F50 | > 600 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec, 23°C) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent 2(3.20 mm) | 1210 | MPa | ASTM D638 |
| Tensile Strength 3(Yield) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 700 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 530 | J/m | ASTM D256A |
| Tensile Impact Strength | 189 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Brittleness Temperature 6 | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 7 |
| Melting Temperature | 127 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | HLMFI |
| 2 . | 13 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | Type IV, 50 mm/min |
| 5 . | 2°C/min |
| 6 . | F50; 25 lbf*in |
| 7 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4175 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RheTech Polypropylene RCC233-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SATRAN® ABS 800 R | MRC Polymers, Inc. | ABS | SATRAN® ABS |
| ALCOM® PA66 910/1 GB30 MO2 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Clyrell EC310K | PolyMirae | PP Copolymer | Clyrell |