NYCOA Polyamide 534 H
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IuuTt9_NYCOA-Polyamide-534-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 534 H is a high viscosity; heat stabilized, nucleated Nylon 6 resin. The high viscosity and fast set-up time make an excellent material for extrusion of tubing, rods, sheet and film. Because of its fast set-up time, fast extrusion line speeds have b NYCOA 534 H is suitable for applications that require continuous exposure to temperatures in excess of 110° C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 1.8 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 82.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 130 | % | ASTM D638 |
| Flexural Modulus 3 | 2690 | MPa | ASTM D790 |
| Flexural Strength 4 | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 191 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.6 | °C | ASTM D648 |
| Continuous Use Temperature | 110 | °C | ASTM D794 |
| Melting Temperature | 221 | °C | DSC |
| Additional Information |
|---|
| Relative Viscosity, NYCOA Method: 4 to 4.4 SAVWater Extractable, NYCOA Method: 0.8 %The value listed as Melting Point DSC, was tested in accordance with ASTM D789.The value listed as Max. Continuous Use Tmp, ASTM D794 may not have been tested according to this standard. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V515R34 | Lucent Polymers, Inc. | PP, Unspecified | Primefin |
| Rynite® 935 NC010 | DuPont Performance Polymers | PET | Rynite® |
| SLOVALEN® PH 69 GF 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| Formolene® 4142T | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| HiCal™ LC | Heritage Plastics, Inc. | PP Impact Copolymer | HiCal™ |