XAREC™ WA 214LG
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | XAREC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IugSiO_XAREC-WA-214LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XAREC™ WA 214LG is a Syndiotactic Polystyrene (SPS) product filled with 40% glass fiber. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.20 to 0.40 | % | |
| Flow | 0.10 to 0.30 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus | 13200 | MPa | ISO 178 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 11 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed 2 | 270 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed 3 | 250 | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed 4 | 240 | °C | ISO 75-2/A |
| CLTE | TMA | ||
| Flow : -30 to 30°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.8E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | IEC 60250 | |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 2 | IEC 60112 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (> 1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| 2 . | Mold temperature: 150°C |
| 3 . | Mold temperature: 150°C |
| 4 . | Mold temperature: 80°C |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7600 FL HF/2 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Crastin庐 SK601 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Dynacom DA2540 | Dynachem Co. Ltd. | PC+ABS | Dynacom |
| ESTALENE EN 25 C | Cossa Polimeri S.r.l. | Polyolefin, Unspecified | ESTALENE EN |
| Sumiliteresin® PR-51107 | SBHPP | Phenolic | Sumiliteresin® |