AXELERON™ GP K-3479 BK CPD

Category:	HDPE , Black High Density Polyethylene Compound for Cable Jacketing
Manufacturer:	The Dow Chemical Company
Trademark:	AXELERON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IuRPGo_AXELERON-GP-K-3479-BK-CPD.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AXELERON™ GP K-3479 BK CPD is a high-molecular weight, high density polyethylene compound ("CPD") produced from resin made by the UNIPOL™ process. AXELERON™ GP K-3479 BK CPD is a prime quality telephone and power cable black jacketing that provides good toughness, stress-cracking resistance, outdoor weatherability and abrasion resistance. Specifications AXELERON™ GP K-3479 BK CPD meets the following raw material specifications: ASTM D-1248: Type III, Class C, Category 5, Grades E10 and J4, J5 Federal LP-390C: Type III, Class H, Grade 1, Category 5 REA PE 39 and PE 89 (Raw Material Sections) Cable jacketed with AXELERON™ GP K-3479 BK CPD, using sound commercial extrusion practices, should meet the following specifications: ICEA: S-61-402; NEMA WC5 REA PE 39 and PE 89 ANSI: C8.35 IEC 60502

General Information
Uses	Cable sheath Cable sheath Wire and cable applications Optical fiber cable
Agency Ratings	ANSI C 8.35 ASTM D 1248, III, Class C, Cat. 5 ICEA S-61-402 IEC 60502 NEMA WC-5 REA PE-39 REA PE-89
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.952	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.20	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (10% Igepal, F0)	> 336	hr	ASTM D1693
Carbon Black Content	2.6	%	ASTM D1603
Absorption Coefficient - (kAB/m)	> 400		ASTM D3349

Aging	Nominal Value	Unit	Test Method
Tensile strength retention- 48 hrs (100°C)	90	%	ASTM D638
Elongation retention rate- 48 hrs (100°C)	95	%	ASTM D638

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	20.7	MPa	ASTM D638
--	29.0	MPa	ASTM D638
Tensile Elongation (Break)	800	%	ASTM D638
Flexural Modulus	1030	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature ¹	< -100	°C	ASTM D746

Electrical	Nominal Value		Test Method
Dielectric Constant (1 MHz)	2.56		ASTM D1531
Dissipation Factor (1 MHz)	3.0E-4		ASTM D1531

Extrusion	Nominal Value	Unit
Melt Temperature	232 - 249	°C

Extrusion instructions
AXELERON™ GP K-3479 BK CPD provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 450-480°F (232-249°C). Hopper drying at 180°F (82°C) to remove moisture is recommended. However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known.

Extrusion instructions

AXELERON™ GP K-3479 BK CPD provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 450-480°F (232-249°C). Hopper drying at 180°F (82°C) to remove moisture is recommended. However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known.

Note Message
1 .	F50

Resin Grade	Manufacturer	Category	Trademark
RTP 2286 HF	RTP Company	PEEK	RTP
RTP 287 TFE 10	RTP Company	Nylon 66	RTP
TOTAL Polypropylene PPR 7238	TOTAL Refining & Chemicals	PP Random Copolymer	TOTAL Polypropylene
Hostaform® MT8F01	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
LNP™ THERMOCOMP™ UF004AS compound	SABIC Innovative Plastics Europe	PPA	LNP™ THERMOCOMP™