DOW™ LDPE 432E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iu4lq0_DOW-LDPE-432E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE 432E is a high clarity resin designed for lamination film and clarity overwrap applications. This resin contains slip and antiblock additives. When properly fabricated, this product displays excellent processability and draw down, and a very good balance of film impact resistance, tensile strength and tear resistance. Main Applications:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.925 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.10 - 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm | 190 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 50 µm | 22.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 450 | % | ASTM D882 |
| TD : Break, 50 µm | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 50 µm | 500 | g | ASTM D1922 |
| TD : 50 µm | 400 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 67 | ASTM D2457 | |
| Haze (50.0 µm) | 9.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions for Blown Film: Blow-up Ratio: 1.5 - 3 Melt Temperature: 170 to 210°C |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8784-77 Black 277 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Celstran® PP-GF40-23 Natural | Celanese Corporation | PP, Unspecified | Celstran® |
| K PP 9070 AP | Technovinyl Polymers India Ltd. | PP, Unspecified | K PP |
| LOXIM 110 01 V0 | LOXIM Industries Private Limited | PC | LOXIM |
| Sylvin 8980-70 HMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |