| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | ALAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iu45R0_ALAMID-6-GK-50.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| polyamide 6 + 50% glass beads, stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 5.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) 1 | 221 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 10K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® R-4-220BL | Solvay Specialty Polymers | PPS | Ryton® |
| SCHULAMID® 6 MV HI | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Celcon® WR25Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| DINALON® A1S25 G25 | Grupo Repol | Nylon 66 | DINALON® |
| Ecobarrier® 2014 | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |