Kinta NB6015G
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Iu18My_KintaNB6015G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta NB6015G is a polyamide 6 (nylon 6) product, which contains a 15% glass fiber reinforced material. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.70 - 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 115 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5300 | MPa | ASTM D790 |
| Flexural Strength 4 | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.20 mm | 5.00 | kJ/m² | ASTM D256 |
| 23°C, 3.20 mm | 7.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 180 | °C | ASTM D648 |
| Melting Temperature | 225 | °C | DSC |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dissipation Factor 5(23°C, 1 MHz) | 0.030 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Injection Pressure | 100 - 160 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3488 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC X3548 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PROTEQ™ H20SQ8 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| EUROPLEX® Sheet PPSU 99470 KR Coating | Evonik Industries AG | PPSU | EUROPLEX® Sheet |
| LNP™ STAT-KON™ DX09301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |