INNOPOL® PP CS 2-8000
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ItaZfV_INNOPOL-PP-CS-2-8000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL ® CS 2-8000 is a polypropylene block-copolymer. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 2-8000 is highly suitable for pipe manufacturing where the required property is high impact resistance besides good stiffness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.2 | kJ/m² | ISO 179/1eA |
| 23°C | 65 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 87.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A120 |
| -- | 79.0 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.50 | % | |
| Rear Temperature | 190 - 260 | °C | |
| Middle Temperature | 190 - 260 | °C | |
| Front Temperature | 190 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 15.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 180 - 220 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Cylinder Zone 5 Temp. | 180 - 220 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN M1701 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Viton® GBLT-600S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| New-prene™ 7050N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Fainplast PVC FK 0635 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LACTEL® 50:50 DL-PLG | DURECT Corporation | PLA | LACTEL® |