Bapolene® 200F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ItHkkA_Bapolene-200F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene LD200F is a general purpose low density polyethylene for blown film extrusion applications. It contains medium levels of slip/antiblock additives. This product meets FDA standards for food contact applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus 1 | ASTM D882 | ||
| MD : 32 µm, blown film | 193 | MPa | ASTM D882 |
| TD : 32 µm, blown film | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 15.2 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 12.4 | MPa | ASTM D882 |
| MD : Broken, 32 µm, blown film | 22.8 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 17.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 360 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 580 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 79 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, blown film | 570 | g | ASTM D1922 |
| TD : 32 µm, blown film | 270 | g | ASTM D1922 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (32.0 µm, blown film) | 67 | ASTM D2457 |
| Additional Information |
|---|
| Film properties are based on a thickness of 32 µm and blow-up ratio of 2:1. |
| Note Message | |
|---|---|
| 1 . | 0.10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1381 P-1 TFE 20 | RTP Company | PPS | RTP |
| Sahara™ Films | Eastman Chemical Company | Polyester, TP | Sahara™ |
| SHIN-A SEN-6085 | SHIN-A T&C | Epoxy | SHIN-A |
| AKROMID® B3 black (2502) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| LNP™ COLORCOMP™ PX99848 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ COLORCOMP™ |