PENTAMID B S GV60 H natural
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | It7kz3_PENTAMIDBSGV60Hnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity, heat stabilised polyamide 6, 60% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.68 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.35 | -- | % | ISO 294-4 |
| Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | ISO 62 |
| Viscosity Number | 120 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 19000 | 14700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 220 | 155 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | 3.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 21 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6, MHR, 12-190, GF60 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.13 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 265 - 285 | °C | |
| Middle Temperature | 270 - 295 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 71.5 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Neostar™ FN007 | Eastman Chemical Company | Copolyester Elastomer (Ether) | Neostar™ |
| Ferro PP TPP30AJ41BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Formolon® 260 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Hyundai EP TPO HR930 | HYUNDAI EP Co., Ltd. | TPO (POE) | Hyundai EP TPO |
| NYLOY® KF-0030N 311WT | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |